EN10219-1 Cold Finished Structural Hollow Section

Allland produces and stocks a full range of EN10219-1 Cold Finished Structural Hollow Section. It can be welded or seamless heavy wall steel pipes for machine work. We export tens of thousands of tons of such steel pipes every year to EU, UK, Thailand, Singapore, Austrilia, New Zealand, Iran, Peru, Chile. If you want to import high quality EN10219 S235/S355 steel pipes, come to Allland.

  • Grades: S235/S355 JRH/J0H/J2H
  • Outer Diameter: 4″-56″
  • Thickness: 0.237″-5.90″
  • Surface Treatment: Natural, Varnished, Black painting, FBE, 3PE (3LPE), 3PP, FBE, HDG(Hot Dipped Galvanized)
Get a Quote
Category:

Table A.1 — Chemical composition — Cast analysis for product thickness≤120 mm

Steel grade Type of deoxidation % by mass, maximum
Steel name Steel number C Specified thickness (mm) Si Mn P S N b c
£ 40 >40 £ 120
S235JRH 1.0039 FN 0,17 0,20 — 1,40 0,040 0,040 0,009
S275J0H 1.0149 FN 0,20 0,22 — 1,50 0,035 0,035 0,009
S275J2H 1.0138 FF 0,20 0,22 — 1,50 0,030 0,030 —
S355J0H 1.0547 FN 0,22 0,22 0,55 1,60 0,035 0,035 0,009
S355J2H 1.0576 FF 0,22 0,22 0,55 1,60 0,030 0,030 —
S355K2H 1.0512 FF 0,22 0,22 0,55 1,60 0,030 0,030 —
a The deoxidation methods are designated as follows: FN = Rimming steel not permitted
FF = Fully killed steel containing nitrogen binding elements in amounts sufficient to bind available nitrogen (e.g. min. 0,020 % total Al, or 0,015 % soluble Al).
b It is permissible to exceed the specified values provided that for each increase of 0,001 % N the P max. content is also reduced by 0,005 %. The N content of the cast analysis, however, shall not be more than 0,012 %.
c The maximum value for nitrogen does not apply if the chemical composition shows a minimum total Al content of 0,020 % with a minimum Al/N ratio of 2:1, or if sufficient other N-binding elements are present. The N-binding elements shall be recorded in the Inspection Document.
Steel grade Min. yield strength
ReH MPa		 Tensile strength
Rm MPa		 Min. elongation
A a b %		 Minimum impact
energy KV d J
Specified thickness
mm		 Specified thickness
mm		 Specified thickness
mm		 At test temperature
of
Steel name Steel number £16 >16
£40		 >40
£63		 >63
£80		 >80
£100		 > 00
£120		 £3 >3
£100		 >100
£120		 £ 40 >40
£63		 >63
£100		 >100
£120		 -20°C 0°C 20°C
S235JRHc 1.0039 235 225 215 215 215 195 360-510 360-510 350-500 26 25 24 22 – – 27
S275J0Hc 1.0149 275 265 255 245 235 225 430-580 410-560 400-540 23 22 21 19 – 27 –
S275J2H 1.0138 27 – –
S355J0Hc 1.0547 355 345 335 325 315 295 510-680 470-630 450-600 22 21 20 18 – 27 –
S355J2H 1.0576 27 – –
S355K2H 1.0512 40 e – –
a      Longitudinal values. Transverse values are 2 % lower.
b      For thicknesses < 3 mm, see 9.2.2.
c      The impact properties are verified only when Option 1.3 is specified.
d      For impact properties for reduced section test pieces see 6.6.2.
e     This value corresponds to 27J at –30 °C (see EN 1993-1-1).